Prepregs (show all)

  Carbon prepreg C90Ppp 1K, optimized for hot press, 30 m2 roll   Price: 2414.40 EUR / 30 m2 roll Price / m2: 80.48 EUR   TECHNICAL CHARACTERISTICS Fabric weight: 92 g / m2 Width: 1.00 meter Weaving style: Plain Warp: 1K T300 carbon fiber, 50%, 7 ends (threads) / cm Weft: 1K T300 carbon fiber, 50%, 7 ends / cm   Prepreg weight: 167 g / m2 Epoxy content: 45% Volatile content: < 1%   Fibermax general purpose prepregs are based on a 80 to 150 oC (176 - 302 oF) curing toughened epoxy matrix, suited for both autoclave and press molding applications. A standard autoclave curing cycle is: Draw vacuum (0.6 - 0.7 bar) and apply positive pressure. Then start heating - typically 2-5 oC / min (3.5 - 9 oF) - till 120 oC (248 oF) and then hold this temperature for 1 hour. Turn off the temperature and cool under pressure to 60 oC (140 oF). When fully cooled open the bag and extract the piece.   STORAGE LIFE 12 months at - 18 oC 4 - 6 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   EVALUATED Tg FOR RESPECTIVE CURING CYCLE 1 hour at 120 oC (248 oF): 110 - 120 oC (230 - 248 oF) 1 hour at 130 oC (266 oF): 130 - 140 oC (266 - 284 oF) 10 min at 150 oC (302 oF): 130 - 150 oC (266 - 302 oF)   TYPICAL MECHANICAL PROPERTIES OF LAMINATE Cured at 130 oC for 60 minutes and 3 bar Flexural strength (Mpa): 850 Flexural modulus (Gpa): 54 Tensile strength (MPa): 550 Tensile modulus (GPa): 60 ILSS - Short Beam Shear (Mpa): 67 Tg (DSC) 20 oC / min: 128 oC   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
2,414.40€
  Carbon prepreg C160Ppp, general purpose, 40 m2 roll   Price: 1364.80 EUR / 40 m2 roll Price / m2: 34.12 EUR   TECHNICAL CHARACTERISTICS Fabric weight: 160 g / m2 Width: 1.00 meter Weaving style: Plain Warp: 3K TR30S carbon fiber, 50%, 4 ends (threads) / cm Weft: 3K TR30S carbon fiber, 50%, 4 ends (threads) / cm   Prepreg weight: 291 g / m2 Epoxy content: 45% Gel time at 125 oC: 6-9 min Volatile content: < 1 %   Fibermax general purpose prepregs are based on a 80 to 150 oC (176 - 302 oF) curing toughened epoxy matrix, suited for both autoclave and press molding applications. A standard autoclave curing cycle is: Draw vacuum (0.6 - 0.7 bar) and apply positive pressure. Then start heating - typically 2-5 oC / min (3.5 - 9 oF) - till 120 oC (248 oF) and then hold this temperature for 1 hour. Turn off the temperature and cool under pressure to 60 oC (140 oF). When fully cooled open the bag and extract the piece.   STORAGE LIFE 12 months at - 18 oC 4 - 6 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   EVALUATED Tg FOR SUGGESTED CURING CYCLE 1 hour at 125 oC: 120 - 125 oC 2 hours at 110 oC: 120 - 125 oC   TYPICAL MECHANICAL PROPERTIES OF LAMINATE Cured by hot press technology at 125 °C curing cycle Flexural strength (Mpa): 800 Flexural modulus (GPa): 54 ILSS - Short Beam Shear (Mpa): 64   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
1,364.80€
  Carbon prepreg C160T2pp, general purpose, 40 m2 roll Price: 1476.72 EUR / 40 m2 roll Price / m2: 36.92 EUR   TECHNICAL CHARACTERISTICS Fabric weight: 160 g / m2 Width: 1.00 meter Weaving style: Twill 2X2 Warp: 3K TR30S carbon fiber, 50%, 5.25 ends(threads) / cm Weft: 3K TR30S carbon fiber, 50%, 5.25 ends / cm   Prepreg weight: 394 g / m2 Epoxy content: 42 % Gel time at 125 oC: 11 min Volatile content: < 1 % Fibermax general purpose prepregs are based on a 80 to 150 oC (176 - 302 oF) curing toughened epoxy matrix, suited for both autoclave and press molding applications. A standard autoclave curing cycle is: Draw vacuum (0.6 - 0.7 bar) and apply positive pressure. Then start heating - typically 2-5 oC / min (3.5 - 9 oF) - till 120 oC (248 oF) and then hold this temperature for 1 hour. Turn off the temperature and cool under pressure to 60 oC (140 oF). When fully cooled open the bag and extract the piece.   STORAGE LIFE 12 months at - 18 oC 4 - 6 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   EVALUATED Tg FOR RESPECTIVE CURING CYCLE 1 hour at 120 oC (248 oF): 110 - 120 oC (230 - 248 oF) 1 hour at 130 oC (266 oF): 130 - 140 oC (266 - 284 oF) 10 min at 150 oC (302 oF): 130 - 150 oC (266 - 302 oF)   TYPICAL MECHANICAL PROPERTIES OF LAMINATE Cured at 130 oC for 60 minutes and 3 bar Flexural strength (Mpa): 850 Flexural modulus (Gpa): 54 Tensile strength (MPa): 550 Tensile modulus (GPa): 60 ILSS - Short Beam Shear (Mpa): 67 Tg (DSC) 20 oC / min: 128 oC   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
1,476.72€
  Carbon Prepreg C210Ppp, general purpose   TECHNICAL CHARACTERISTICS Fabric weight: 205 g / m2 Width: 1.00 meter Weaving style: Plain Warp: 3K TR30S carbon fiber, 50%, 5.25 ends (threads) / cm Weft: 3K TR30S carbon fiber, 50%, 5.25 ends / cm   Prepreg weight: 394 g / m2 Epoxy content: 42% Gel time at 125 oC: 11 min Volatile content: < 1 %   Fibermax general purpose prepregs are based on a 80 to 150 oC (176 - 302 oF) curing toughened epoxy matrix, suited for both autoclave and press molding applications. A standard autoclave curing cycle is: Draw vacuum (0.6 - 0.7 bar) and apply positive pressure. Then start heating - typically 2 - 5 oC / min (3.5 - 9 oF) - till 120 oC (248 oF) and then hold this temperature for 1 hour. Turn off the temperature and cool under pressure to 60 oC (140 oF). When fully cooled open the bag and extract the piece.   STORAGE LIFE 12 months at - 18 oC 4 - 6 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   EVALUATED Tg FOR RESPECTIVE CURING CYCLE 1 hour at 120 oC (248 oF): 110 - 120 oC (230 - 248 oF) 1 hour at 130 oC (266 oF): 130 - 140 oC (266 - 284 oF) 10 min at 150 oC (302 oF): 130 - 150 oC (266 - 302 oF)   TYPICAL MECHANICAL PROPERTIES OF LAMINATE (Cured at 130 oC for 60 minutes and 3 bar) Flexural strength (Mpa): 850 Flexural modulus (Gpa): 54 Tensile strength (MPa): 550 Tensile modulus (GPa): 60 ILSS - Short Beam Shear (Mpa): 67 Tg (DSC) 20 oC / min: 128 oC   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
From 40.53€ ...to 49.33€
  Carbon prepreg C201T2pp, general purpose   TECHNICAL CHARACTERISTICS Fabric weight: 200 g / m2 Width: 1.00 meter Weaving style: Twill 2X2 Warp: 3K HTA 40 carbon fiber, 50%, 5 ends (threads) / cm Weft: 3K HTA 40 carbon fiber, 50%, 5 ends / cm   Prepreg weight: 344 g / m2 Epoxy content: 42% Gel time at 115 oC: 18-23 min Volatile content: < 1%   RECOMMENDED CURING TIME Curing time is 60 minutes at 130 oC or 500 minutes at 85 oC. Different curing cycles could be applicable. The conditions and duration of prepreg processing can be adapted based on the specific requirements and circumstances of the curing process. The curing time and resin loss during the manufacturing process are directly related to the rapid heat transfer temperature of the mold thickness.   STORAGE LIFE Room temperature (around  22 oC): > 1 month 0 oC: > 3 months - 18 oC: > 6 months Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   TYPICAL MECHANICAL PROPERTIES OF LAMINATE Tensile strength (Mpa): 60 - 80 Bending strength (MPa): 90 - 110 Elongation at break (%): 4 - 5   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
From 36.29€ ...to 43.84€
  Carbon prepreg C210T2pp, general purpose   TECHNICAL CHARACTERISTICS Fabric weight: 206 g / m2 Width: 1.00 meter Weaving style: Twill 2X2 Warp: 3K TR30S carbon fiber, 49.5%, 5.10 ends (threads) / cm Weft: 3K TR30S carbon fiber, 50.5%, 5.20 ends / cm   Prepreg weight: 381 g / m2 Epoxy content: 46% Gel time at 125 oC: 6-9 min Volatile content: < 1%   Fibermax general purpose prepregs are based on a 80 to 150 oC (176 - 302 oF) curing toughened epoxy matrix, suited for both autoclave and press molding applications. A standard autoclave curing cycle is: Draw vacuum (0.6 - 0.7 bar) and apply positive pressure. Then start heating - typically 2-5 oC / min (3.5 - 9 oF) - till 120 oC (248 oF) and then hold this temperature for 1 hour. Turn off the temperature and cool under pressure to 60 oC (140 oF). When fully cooled open the bag and extract the piece.   STORAGE LIFE 12 months at - 18 oC 4 - 6 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   EVALUATED Tg FOR SUGGESTED CURING CYCLE 1 hour at 125 oC: 120 - 125 oC 2 hours at 110 oC: 120 - 125 oC   TYPICAL MECHANICAL PROPERTIES OF LAMINATE Cured by hot press technology at 125 °C curing cycle Flexural strength (Mpa): 800 Flexural modulus (GPa): 54 ILSS - Short Beam Shear (Mpa): 64   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
From 42.30€ ...to 51.10€
  Carbon prepreg C211T2pp, optimized for hot press   TECHNICAL CHARACTERISTICS Fabric weight: 206 g / m2 Width: 1.00 meter Weaving style: Twill 2X2 Warp: 3K TR30S carbon fiber, 49.5%, 5.10 ends (threads) / cm Weft: 3K TR30S carbon fiber, 50.5%, 5.20 ends / cm   Prepreg weight: 381 g / m2 Epoxy content: 46% Volatile content: < 1%   RECOMMENDED CURING CYCLES 8 min at 150 oC 10 min at 145 oC 15 min at 140 oC   STORAGE LIFE 12 months at - 18 oC 3 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibermax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
From 42.30€ ...to 52.50€
  Carbon prepreg C212T2pp, optimized for out of autoclave (vacuum only) curing. One side of the fabric is partially impregnated with a resin film, and the other side is dry (to facilitate the air and volatile content to escape). C212T2pp is a not high tack prepreg. Tack enhancing may be achieved by means of temperature or special purpose tack modification spray.   TECHNICAL CHARACTERISTICS Fabric weight: 206 g / m2 Width: 1.27 meters Weaving style: Twill 2X2 Warp: 3K TR30S carbon fiber, 49.5%, 5.10 ends (threads) / cm Weft: 3K TR30S carbon fiber, 50.5%, 5.20 ends / cm   Prepreg weight: 332 g / m2 Epoxy content: 38% Gel time at 125 oC: 7-8 min Volatile content: < 1%   RECOMMENDED CURING CYCLES 12 h at 80 oC (Tg 110-115 oC) or 1 h at 135 oC (Tg 120-125 oC)   RECOMMENDED PROCEDURE Draw vacuum to evacuate entrapped air for at least 1 hour, depending on size and complexity of the mould Raise temperature to 70 oC Keep 70 oC for at least 1 hour, depending on the size and complexity of the mould Raise temperature to 135 oC, with a step of 1-3 oC / min Keep 135 oC for about 1 hour, depending on number of layers, area size, complexity and type of mould   STORAGE LIFE 12 months at - 18 oC 5-6 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
From 48.15€ ...to 56.95€
  Carbon prepreg C240T2pp, general purpose, 40 m2 roll   Price: 1908.00 EUR / 40 m2 roll Price / m2: 47.70 EUR   TECHNICAL CHARACTERISTICS Fabric weight: 240 g / m2 Width: 1.00 meter Weaving style: Twill 2X2 Warp: 3K T300 carbon fiber, 50%, 6 ends (threads) / cm Weft: 3K T300 carbon fiber, 50%, 6 ends / cm   Prepreg weight: 429 g / m2 Epoxy content: 42% Gel time at 125 oC: 11 min Volatile content: < 1%   Fibermax general purpose prepregs are based on a 80 to 150 oC (176 - 302 oF) curing toughened epoxy matrix, suited for both autoclave and press molding applications. A standard autoclave curing cycle is: Draw vacuum (0.6 - 0.7 bar) and apply positive pressure. Then start heating - typically 2-5 oC / min (3.5 - 9 oF) - till 120 oC (248 oF) and then hold this temperature for 1 hour. Turn off the temperature and cool under pressure to 60 oC (140 oF). When fully cooled open the bag and extract the piece.   STORAGE LIFE 12 months at - 18 oC 4 - 6 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   EVALUATED Tg FOR RESPECTIVE CURING CYCLE 1 hour at 120 oC (248 oF): 110 - 120 oC (230 - 248 oF) 1 hour at 130 oC (266 oF): 130 - 140 oC (266 - 284 oF) 10 min at 150 oC (302 oF): 130 - 150 oC (266 - 302 oF)   TYPICAL MECHANICAL PROPERTIES OF LAMINATE Cured at 130 oC for 60 minutes and 3 bar Flexural strength (Mpa): 850 Flexural modulus (Gpa): 54 Tensile strength (MPa): 550 Tensile modulus (GPa): 60 ILSS - Short Beam Shear (Mpa): 67 Tg (DSC) 20 oC / min: 128 oC   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
1,908.00€
  Carbon prepreg C242T2pp, optimized for out of autoclave (vacuum only) curing. One side of the fabric is partially impregnated with a resin film, and the other side is dry (to facilitate the air and volatile content to escape)   TECHNICAL CHARACTERISTICS Fabric weight: 240 g / m2 Width: 1.00 meter Weaving style: Twill 2X2 Warp: 3K TR30S carbon fiber, 50%, 6 ends (threads) / cm Weft: 3K TR30S carbon fiber, 50%, 6 ends / cm   Prepreg weight: 387 g / m2 Epoxy content: 38% Gel time at 125 oC: 7-8 min Volatile content: < 1%   RECOMMENDED CURING CYCLES 12 h at 80 oC (Tg 110-115 oC) 1 h at 135 oC (Tg 120-125 oC)   RECOMMENDED PROCEDURE Draw vacuum to evacuate entraped air for at least 1 hour, depending on size and complexity of the mould Raise temperature to 70 oC Keep 70 oC for at least 1 hour, depending on the size and complexity of the mould Raise temperature to 135 oC, with a step of 1-3 oC / min Keep 135 oC for about 1 hour, depending on number of layers, area size, complexity and type of mould   STORAGE LIFE 12 months at - 18 oC 5 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
From 52.02€ ...to 60.82€
  Carbon prepreg C280T2pp, general purpose, 40 m2 roll   Price: 2136.00 EUR / 40 m2 roll Price / m2: 53.40 EUR   TECHNICAL CHARACTERISTICS Fabric weight: 280 g / m2 Width: 1.00 meter Weaving style: Twill 2X2 Warp: 6K T300 carbon fiber, 50%, 5.25 ends (threads) / cm Weft: 6K T300 carbon fiber, 50%, 5.25 ends / cm   Prepreg weight: 491 g / m2 Epoxy content: 42% Gel time at 125 oC: 11 min Volatile content: < 1%   Fibermax general purpose prepregs are based on a 80 to 150 oC (176 - 302 oF) curing toughened epoxy matrix, suited for both autoclave and press molding applications. A standard autoclave curing cycle is: Draw vacuum (0.6 - 0.7 bar) and apply positive pressure. Then start heating - typically 2-5 oC / min (3.5 - 9 oF) - till 120 oC (248 oF) and then hold this temperature for 1 hour. Turn off the temperature and cool under pressure to 60 oC (140 oF). When fully cooled open the bag and extract the piece.   STORAGE LIFE 12 months at - 18 oC 4 - 6 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   EVALUATED Tg FOR RESPECTIVE CURING CYCLE 1 hour at 120 oC (248 oF): 110 - 120 oC (230 - 248 oF) 1 hour at 130 oC (266 oF): 130 - 140 oC (266 - 284 oF) 10 min at 150 oC (302 oF): 130 - 150 oC (266 - 302 oF)   TYPICAL MECHANICAL PROPERTIES OF LAMINATE Cured at 130 oC for 60 minutes and 3 bar Flexural strength (Mpa): 850 Flexural modulus (Gpa): 52 Tensile strength (MPa): 730 Tensile modulus (GPa): 62 ILSS - Short Beam Shear (Mpa): 66 Tg (DSC) 20 oC / min: 128 oC   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
2,136.00€
  Carbon prepreg C285T2pp, general purpose, 40 m2 roll   Price: 2124.00 EUR / 40 m2 roll Price / m2: 53.10 EUR   TECHNICAL CHARACTERISTICS Fabric weight: 285 g / m2 Width: 1.00 meter Weaving style: Twill 2X2 Warp: 3K T300 carbon fiber, 50%, 7 ends (threads) / cm Weft: 3K T300 carbon fiber, 50%, 7 ends / cm   Prepreg weight: 500 g / m2 Epoxy content: 42% Gel time at 125 oC: 11 min Volatile content: < 1%   Fibermax general purpose prepregs are based on a 80 to 150 oC (176 - 302 oF) curing toughened epoxy matrix, suited for both autoclave and press molding applications. A standard autoclave curing cycle is: Draw vacuum (0.6 - 0.7 bar) and apply positive pressure. Then start heating - typically 2-5 oC / min (3.5 - 9 oF) - till 120 oC (248 oF) and then hold this temperature for 1 hour. Turn off the temperature and cool under pressure to 60 oC (140 oF). When fully cooled open the bag and extract the piece.   STORAGE LIFE 12 months at - 18 oC 4 - 6 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   EVALUATED Tg FOR RESPECTIVE CURING CYCLE 1 hour at 120 oC (248 oF): 110 - 120 oC (230 - 248 oF) 1 hour at 130 oC (266 oF): 130 - 140 oC (266 - 284 oF) 10 min at 150 oC (302 oF): 130 - 150 oC (266 - 302 oF)   TYPICAL MECHANICAL PROPERTIES OF LAMINATE Cured at 130 oC for 60 minutes and 3 bar Flexural strength (Mpa): 850 Flexural modulus (Gpa): 54 Tensile strength (MPa): 550 Tensile modulus (GPa): 60 ILSS - Short Beam Shear (Mpa): 67 Tg (DSC) 20 oC / min: 128 oC   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
2,124.00€
  Carbon prepreg C285T4pp, general purpose   TECHNICAL CHARACTERISTICS Fabric weight: 285 g / m2 Width: 1.00 meter Weaving style: Twill 4X4 Warp: 3K T300 carbon fiber, 50%, 7 ends (threads) / cm Weft: 3K T300 carbon fiber, 50%, 7 ends / cm   Prepreg weight: 510 g / m2 Epoxy content: 44% Gel time at 125 oC: 6-9 min Volatile content: < 1 %   Fibermax general purpose prepregs are based on a 80 to 150 oC (176 - 302 oF) curing toughened epoxy matrix, suited for both autoclave and press molding applications. A standard autoclave curing cycle is: Draw vacuum (0.6 - 0.7 bar) and apply positive pressure. Then start heating - typically 2-5 oC / min (3.5 - 9 oF) - till 120 oC (248 oF) and then hold this temperature for 1 hour. Turn off the temperature and cool under pressure to 60 oC (140 oF). When fully cooled open the bag and extract the piece.   STORAGE LIFE 12 months at - 18 oC 5 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   EVALUATED Tg FOR SUGGESTED CURING CYCLE 1 hour at 125 oC: 120 - 125 oC 2 hours at 110 oC: 120 - 125 oC   TYPICAL MECHANICAL PROPERTIES OF LAMINATE Cured by hot press technology at 125 oC curing cycle Flexural strength (Mpa): 805 Flexural modulus (Gpa): 51 ILSS - Short Beam Shear (Mpa): 61   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
From 53.10€ ...to 61.90€
  Carbon prepreg C330Upp, general purpose   TECHNICAL CHARACTERISTICS Fabric weight: 324 g / m2 Width: 1.00 meter Weaving style: Unidirectional Warp: HTS 45 E23 12K carbon fiber, 93.33%, 3.80 ends (threads) / cm Weft: E Glass EC9 68tex, 6.67%, 3.00 ends / cm   Prepreg weight: 540 g / m2 Epoxy content: 40% Gel time at 125 oC: 6-9 min Volatile content: < 1 %   Fibermax general purpose prepregs are based on a 80 to 150 oC (176 - 302 oF) curing toughened epoxy matrix, suited for both autoclave and press molding applications. A standard autoclave curing cycle is: Draw vacuum (0.6 - 0.7 bar) and apply positive pressure. Then start heating - typically 2-5 oC / min (3.5 - 9 oF) - till 120 oC (248 oF) and then hold this temperature for 1 hour. Turn off the temperature and cool under pressure to 60 oC (140 oF). When fully cooled open the bag and extract the piece.   STORAGE LIFE 12 months at - 18 oC 5 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   EVALUATED Tg FOR SUGGESTED CURING CYCLE 1 hour at 125 oC: 120 - 125 oC 2 hours at 110 oC: 120 - 125 oC   TYPICAL MECHANICAL PROPERTIES OF LAMINATE Cured by hot press technology at 125 oC curing cycle Flexural strength (Mpa): 1150 Flexural modulus (Gpa): 115 ILSS - Short Beam Shear (Mpa): 73   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
From 38.16€ ...to 46.96€
  Carbon prepreg C420Upp, general purpose, 40 m2 roll   Price: 1716.96 EUR / 40 m2 roll Price / m2: 42.92 EUR   TECHNICAL CHARACTERISTICS Fabric weight: 420 g / m2 Width: 1.00 meter Weaving style: Unidirectional, woven Warp: 12K TR50S carbon fiber, 92%, 5.00 ends (threads) / cm Weft: Glass thermoplastic 8%, 1.60 ends (threads) / cm   Prepreg weight: 680 g / m2 Epoxy content: 38% Gel time at 125 oC: 11 min Volatile content: < 1%   Fibermax general purpose prepregs are based on a 80 to 150 oC (176 - 302 oF) curing toughened epoxy matrix, suited for both autoclave and press molding applications. A standard autoclave curing cycle is: Draw vacuum (0.6 - 0.7 bar) and apply positive pressure. Then start heating - typically 2-5 oC / min (3.5 - 9 oF) - till 120 oC (248 oF) and then hold this temperature for 1 hour. Turn off the temperature and cool under pressure to 60 oC (140 oF). When fully cooled open the bag and extract the piece.   STORAGE LIFE 12 months at - 18 oC 4 - 6 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   EVALUATED Tg FOR RESPECTIVE CURING CYCLE 1 hour at 120 oC (248 oF): 110 - 120 oC (230 - 248 oF) 1 hour at 130 oC (266 oF): 130 - 140 oC (266 - 284 oF) 10 min at 150 oC (302 oF): 130 - 150 oC (266 - 302 oF)   TYPICAL MECHANICAL PROPERTIES OF LAMINATE Cured at 130 oC for 60 minutes and 3 bar Flexural strength (Mpa): 850 Flexural modulus (Gpa): 59 Tensile strength (MPa): 650 Tensile modulus (GPa): 59 ILSS - Short Beam Shear (Mpa): 65 Tg (DSC) 20 oC / min: 140 oC   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
1,716.96€
  Carbon prepreg C428T2pp, general purpose   TECHNICAL CHARACTERISTICS Fabric weight: 428 g / m2 Width: 1.00 meter Weaving style: Twill 2X2 Warp: 12K T700 carbon fiber, 50%, 2.7 ends (threads) / cm Weft: 12K T700 carbon fiber, 50%, 2.7 ends / cm   Prepreg weight: 740 g / m2 Epoxy content: 42% Gel time at 125 oC: 6-9 min Volatile content: < 1%   Fibermax general purpose prepregs are based on a 80 to 150 oC (176 - 302 oF) curing toughened epoxy matrix, suited for both autoclave and press molding applications. A standard autoclave curing cycle is: Draw vacuum (0.6 - 0.7 bar) and apply positive pressure. Then start heating - typically 2-5 oC / min (3.5 - 9 oF) - till 120 oC (248 oF) and then hold this temperature for 1 hour. Turn off the temperature and cool under pressure to 60 oC (140 oF). When fully cooled open the bag and extract the piece.   STORAGE LIFE 12 months at - 18 oC 5 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   EVALUATED Tg FOR SUGGESTED CURING CYCLE 1 hour at 125 oC: 120 - 125 oC 2 hours at 110 oC: 120 - 125 oC   TYPICAL MECHANICAL PROPERTIES OF LAMINATE Cured by hot press technology at 125 oC curing cycle Flexural strength (Mpa): 800 Flexural modulus (Gpa): 52 ILSS - Short Beam Shear (Mpa): 64   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
From 44.55€ ...to 53.35€
  Fiberglass prepreg G050Ppp, general purpose   TECHNICAL CHARACTERISTICS Fabric weight: 46 g / m2 Weaving style: Plain Width: 1.00 meter Warp: Glass EC5 11 fiber, 56%, 22 ends (threads) / cm Weft: Glass EC5 11 fiber, 44%, 22 ends / cm   Prepreg weight: 115 g / m2 Epoxy content: 60% Gel time at 125 oC: 11 min Volatile content: < 1 % Fibermax general purpose prepregs are based on a 80 to 150 oC (176 - 302 oF) curing toughened epoxy matrix, suited for both autoclave and press molding applications. A standard autoclave curing cycle is: Draw vacuum (0.6 - 0.7 bar) and apply positive pressure. Then start heating - typically 2-5 oC / min (3.5 - 9 oF) - till 120 oC (248 oF) and then hold this temperature for 1 hour. Turn off the temperature and cool under pressure to 60 oC (140 oF). When fully cooled open the bag and extract the piece.   STORAGE LIFE 12 months at - 18 oC 4 - 6 weeks at room temperature Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation.   EVALUATED Tg FOR RESPECTIVE CURING CYCLE 1 hour at 120 oC (248 oF): 110 - 120 oC (230 - 248 oF) 1 hour at 130 oC (266 oF): 130 - 140 oC (266 - 284 oF) 10 min at 150 oC (302 oF): 130 - 150 oC (266 - 302 oF)   TYPICAL MECHANICAL PROPERTIES OF LAMINATE Cured at 130 oC for 60 minutes and 3 bar Flexural strength (Mpa): 850 Flexural modulus (Gpa): 54 Tensile strength (MPa): 550 Tensile modulus (GPa): 60 ILSS - Short Beam Shear (Mpa): 67 Tg (DSC) 20 oC / min: 128 oC   Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibremax Ltd reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
From 14.62€ ...to 19.50€
  Adhesive film F180Vpp, suitable for vacuum bag, press or autoclave process, based on preimpregnated ultralight supporting veil (to ease handling)   TECHNICAL CHARACTERISTICS Supporting veil nominal weight: 14 g/sq.m. (8%) Resin weight: 166 g/sq.m. (92%) Total prepreg weight: 180 g/sq.m. Volatile content: < 1.5 % Gel time at 125 C: 7 min   RECOMMENDED CURING CYCLES 16 h at 80 C (Tg 90 C) - postcuring at 125 C recommended 9 h at 90 C (Tg 100 C) - postcuring at 125 C recommended 5 h at 100 C (Tg 110 C) - postcuring at 125 C recommended 1 h at 120 C (Tg 120 C) Postcuring at 130 C (with a step of 1 C/min) could be performed in order to maximize properties   STORAGE LIFE 12 months at - 18 oC 5 weeks at 20 C Allow prepreg roll to reach room temperature before opening plastic bag to prevent condensation. Please click on picture, for a closer view to the fabric's real size. To realize actual size with precision please observe the threads / cm feature mentioned above.   DISCLAIMER All information herein is given for guidance and general information purposes only, represents typical properties, and should not be used for specification limits purposes or basis for design. Fibermax Composites reserves the right to make modifications on fabrics, change yarns, specifications, and all information given herein, without notice. It is only on written certificates and agreements that we provide our customers with warrants for the quality and/or advise for the suitability of products for particular uses. Data sheets and certificates of conformity are promptly provided upon request with roll serial number.   Intrastat Number for this product: 68151200..
From 27.21€ ...to 36.57€