Epoxy system SR1700 / SD7820 (Slow)

 

High performance epoxy laminating system SR1700 / SD7820 with slow hardener

 

Each kilo includes 0.74 kg resin + 0.26 kg hardener

 

High modulus, very stiff system, with low water absorption when cured and excellent adhesion to all types of reinforcements (carbon, aramid, glass etc). This system was developed for automotive, naval, and aerospace applications.

 

Slow hardener SD7820:
Slow hardener, very low viscosity allowing fast reinforcements to wet out. Laminates require 6 to 8 hours of working time. It is adapted to the production of parts with a service temperature up to 120°C. Items can be handled and extracted from moulds after 12 hours at 40°C or 8 h at 60°C.

PROPERTIES
Physical properties of SR1700 epoxy resin:
Aspect / colour: Yellow liquid
Viscosity (mPa.s) at 20 ^oC: 1950 (+- 200)
Density at 20 ^oC: 1.16 (+-0.01)

Physical properties of SD7820 hardener:
Aspect / colour: Clear liquid
Viscosity (mPa.s) at 20 ^oC: 80 ± 15
Density (g/cm³) at 20 ^oC: 0.96 ± 0.01

Mix properties of SR1700 / SD7820 system:
Weight ratio: 100 / 36 g
Volume ratio: 100 / 43 ml
Mix viscosity at 20 ^oC: 750 ± 150

Reactivity of SR1700 / SD7820 system:
Exothermic peak on 500 g mix (^oC) at 20 ^oC: 140 ^oC
Time to reach exothermic peak at 20 ^oC: 9 h 30'

Pot life on 500 g mix at 20 ^oC: 8 h 45'